Withstanding heavy loads
High tensile strength
Excellent surface finishes
Stress corrosion cracking and crevice corrosion resistance
The Stainless Steel 436 / 436L plates are also having good mechanical properties thus they can withstand easily against pitting corrosion and cracking, and also they are having good tensile strength. They are also heat resistive. These are having austenitic steel and preferable for cold working. These stainless steel plates are also good at welding. They do not require any preheating and can be welded directly.
These steel plates have been undergone with the following test like
• Magnetic response- this is done to check the magnetic response of the steel. Austenitic stainless steel is generally non-reactive to the magnetic field even at high temperature.
• Nitric acid reaction- it is strongly resistive towards the attack of nitric acid.
• Molybdenum spot test- this is done to check the composition of molybdenum in the steel plate.
|ASTM A240, ASME SA240|
|JIS, ASTM, AISI, GB, EN, DIN|
|2B, BA, HL, No. 4, Mirror etc.|
|Cold rolled, Hot rolled|
|1000mm, 1219mm, 1250mm, 1500mm, 1524mm, 2000mm|
|Density||Melting Point||Tensile Strength||Yield Strength (0.2%Offset)||Elongation||Hardness|
|0.28 lbs/in3 7.74 g/cm3||2600 – 2750 ° F (1427 – 1510 °C)||77 KSI min (531 MPa min)||53 KSI min (365 MPa min)||40 %||Rb 89 max|
|0.28 lbs/in3 7.74 g/cm3||2600 – 2750 ° F (1427 – 1510 °C)||441-517 MPa 64000-75000 psi (Metric)||276-345 MPa 40000-50000 psi (Imperial)||28-35%||74-85|